Counting the Sources of Pores in Aluminum Alloy Die Casting Process

2024-08-09 hits:0 source:News

  8f63fc6bf55ae

  Aluminum alloy die-casting technology has never been a mature process, and there are always some defects in the production of aluminum alloy die-casting parts. The difference is only a matter of how many, and porosity is an unavoidable defect in aluminum alloy die-casting parts. Next, let's take a closer look at the sources of porosity in aluminum alloy die-casting engineering.

  The main sources of porosity in aluminum alloy die-casting process are as follows: one is the gas trapped in the metal liquid during the filling process, which cannot escape from the die-casting mold cavity in time. These gases will form bubbles in the metal liquid and become porosity after cooling and forming; One type is the porosity caused by volume shrinkage during the formation of aluminum alloy die-casting parts; One is that the gas contained in the molten metal of aluminum alloy has not been completely removed; One reason is that the poor design of aluminum alloy die-casting molds leads to the inability to discharge gases from certain parts; One type is caused by excessive wall thickness in die-casting parts, and these pores are mostly located inside the die-casting parts.

Read recommendations:

architectural aluminium profiles

extruded copper heat sink

die cast aluminum housing

30 x 60 aluminium profile

Die-Casting of Shower Heads

LEAVE A customers

lf you have any questions or comments, you can leave us a message and we will reply to you as soon as possible

Upload Files

Accepted file types: zip, rar, dxf, dwg, sldprt, slddrw, igs, stp, step, sat, x_t, cgr, ipt, par, jpg, jpeg, gif, png, pdf, xls, xlsx, doc, docx.
Maximum supported file is 5MB, for larger or multiple files please send email to Harvey@greenwayalu.com